EFFECTS OF SINTERING TEMPERATURE ON THE STRUCTURE, MICROSTRUCTURE AND PROPERTIES OF 0.935(Bi0.5Na0.5) TiO3 - 0.065BaTiO3 PIEZOELECTRIC CERAMICS
Mots-clés :
free ceramics, sintering temperature, piezoelectric propertiesRésumé
The influence of sintering temperature of 0.935(Bi0.5Na0.5) TiO3-0.065BaTiO3 lead-free ceramics was studied from 1150°C to 1200°C. The X-ray diffraction patternsshowed that all of the BNT6.5BT ceramics exhibited a single perovskite structure with the coexistence of the rhombohedral and tetragonalphase. A fine and homogeneousgrains were observed for samples sintered at 1150 and 1160°C and the increase of the sintering temperature up to 1180-1200°C induces significant grain growth with the appearance of coarse grains. The values ofremnant polarization Probtained at room temperature are 27, 31, 27 and 29 µC/cm 2 for specimens sintered at 1150, 1160, 1180 and 1200°C respectively. At room temperature, the sample sintered at 1180°C exhibited good performances: dielectric constant was 833 at 1 KHz, thick coupling factor ktwas 0.52 and the kt/kpratio was 2.08. Therefore, the ceramics can be suitable for
ultrasonic transducers in commercial applications.
Références
B. JAFFE, W. R. COOK and H. JAFFE, Piezoelectric Ceramics, Academic Press, London, 1971.
F. LEVASSORT et al. J. Eur. Ceram. Soc. 21, (2001) 1361.
Directive 2002/95/EC of European parliament and of the
council of 27 January 2003 on restriction of the use of certain
hazardous substances in electrical and electronic equipment.
Official journal of the European Union.
G.A. SMOLENSKII et al, Sov. Phys. Solid. State
(Engl.Trans.) 2, (11) (1961) 2651.
A. SASAKI et al, Jpn. J. Appl.Phys. 38 (1999) 5564.
T. OH and M-H. KIM, J. Mat. Sci. Eng B 132 (2006) 239.
S.SAID and J-P. MERCURIO, J. Eur. Ceram. Soc.21 (2001)
Y. YUAN et al, J. Mater. Sci 41 (2006) 3561.
Y. LI. et al, J. Mat. Sci. Eng B. 112 (2004) 5.
T. TAKENAKA and H. NAGATA,J. Eur. Ceram. Soc. 25
(2005)2693.
T. TAKENAKA et al, Jpn. J, Appl. Phys. 30 (9B) (1991)
M. CHEN et al. J. Eur. Ceram. Soc. 28 (2008) 843.
B-J. CHU et al. J. Eur.Ceram. Soc. 22 (2002) 2115.
Publié-e
Comment citer
Numéro
Rubrique
Licence
Les auteurs publiant dans cette revue acceptent les termes suivants :- Les auteurs détiennent le droit d'auteurs et accordent à la revue
le droit de première publication, avec l’ouvrage disponible simultanément [SPÉCIFIER LA PÉRIODE DE TEMPS] après publication, sous la licence Licence d’attribution Creative Commons qui permet à d'autres de partager l'ouvrage en en reconnaissant la paternité et la publication initiale dans cette revue. - Les auteurs peuvent conclure des ententes contractuelles additionnelles et séparées pour la diffusion non exclusive de la version imprimée de l'ouvrage par la revue (par ex., le dépôt institutionnel ou la publication dans un livre), accompagné d'une mention reconnaissant sa publication initiale dans cette revue.
- Les auteurs ont le droit et sont encouragés à publier leur ouvrage en ligne (par ex., dans un dépôt institutionnel ou sur le site Web d'une institution) avant et pendant le processus de soumission, car cela peut mener à des échanges fructueux ainsi qu'à un nombre plus important, plus rapidement, de références à l’ouvrage publié (Consulter The Effect of Open Access).