STUDY ON THE NEOPRENE DEGRADATION UNDER COMBINATION EFFECT OF OVEN AGEING AND FATIGUE

Auteurs-es

  • A AYACHE Université Mouloud Mammeri Tizi-Ouzou
  • T BELLAHCÈNE Université Mouloud Mammeri Tizi-Ouzou
  • M ABERKANE Université Mouloud Mammeri Tizi-Ouzou
  • M OULD OUALI Université Mouloud Mammeri Tizi-Ouzou

Mots-clés :

Neoprene, fatigue, oven ageing, fatigue strength

Résumé

     The forecasting of the neoprene lifetime constitutes a major industrial stake for the set of the mechanical manufactured elements with this material like the flexible shaft and automotive belts. The use of this material in these cases, besides, shown that this material deteriorated again more quickly under the combination effect of temperature and fatigue. To characterize this, we carried fatigue tests in alternate tension on a set of new neoprene specimens and ageing ones during 48h and 96h at 100°C into a universal ventilated steam room. The experimental results show, that the (S,N) curves for the three sets of specimens have the same shape and that the fatigue strength brutally falls between the new sample and the aged ones, indicating a loss of fatigue characteristics of this material under accelerated ageing.

Bibliographies de l'auteur-e

A AYACHE, Université Mouloud Mammeri Tizi-Ouzou

Laboratoire d’Energétique Mécanique et Matériaux.
Faculté du Génie de la Construction.

T BELLAHCÈNE, Université Mouloud Mammeri Tizi-Ouzou

Laboratoire d’Energétique Mécanique et Matériaux.
Faculté du Génie de la Construction.

M ABERKANE, Université Mouloud Mammeri Tizi-Ouzou

Laboratoire d’Energétique Mécanique et Matériaux.
Faculté du Génie de la Construction.

M OULD OUALI, Université Mouloud Mammeri Tizi-Ouzou

Laboratoire d’Energétique Mécanique et Matériaux.
Faculté du Génie de la Construction.

Références

Mardel JL, Somers AE, Forsyth M and Hill AJ. Elastomer durability and wear performance in mining environments. Material Australasia. 1997; 29: 18-20.

Harrison A. 15 years of conveyor belt non-destructive evaluation. Bulk Solids Handling 1996. 16: 13-19.

Somers AE, Bastow TJ, Burgar MI, Forsyth M and Hill AJ.

Quantifying rubber degradation using NMR. Polymer degradation and stability. 2000; 70: 31-37.

Bathias C and Baïlon JP. La fatigue des matériaux et des structures. Edition Hermes. 1997. 665-674.

Saintier N, Cailletaud G and Piques R. Crack initiation and propagation under multiaxial fatigue in natural rubber. International Journal of Fatigue. 2006, 28: 61-72.

Téléchargements

Publié-e

2008-12-01

Comment citer

AYACHE, A., BELLAHCÈNE, T., ABERKANE, M., & OULD OUALI, M. (2008). STUDY ON THE NEOPRENE DEGRADATION UNDER COMBINATION EFFECT OF OVEN AGEING AND FATIGUE. Sciences & Technologie. B, Sciences De l’ingénieur, (28), 39–42. Consulté à l’adresse https://revue.umc.edu.dz/b/article/view/263

Numéro

Rubrique

Articles

Articles similaires

1 2 > >> 

Vous pouvez également Lancer une recherche avancée d’articles similaires à cet article.