MAGNETIC PROPERTIES OF THE SPINEL COMPOUND Cu1.30Cr1.30Zr0.70Se4
Keywords:
Cu1.30Cr1.30Zr0.70Se4, Spin glass behaviour and DC measurementsAbstract
The magnetic properties of the spinel compound Cu1.30Cr1.30Zr0.70Se4 have been studied using, magnetic measurements. These measurements (DC) reveal that Cu1.30Cr1.30Zr0.70Se4, orders ferromagnetically-re-entrant spin-glass. The geometrical spin frustration is introduced throughantiferromagnetic interactions due to the substitution of magnetic Cr for Zr atom, on the B sites forming a network of linked tetrahedral. The magnetization in field-cooled (FC) and zero-fieldcooled (ZFC) are observed with irreversibility in T≤ Tf, the overage Curie temperature, the effective magnetic moment and the temperature range, for which magnetic susceptibility can be regarded as linear are given.
Downloads
References
A. Krimmel, M. Mucksch, V. Tsurkan, M.M.Koza, H. Mutka, C. Ritter, D. V. Sheptyakov, S. Horn and A. Loidl, Physical Review B 73, 014413 (2006).
P. Colombet, Doctorat thesis, Nantes University,1982.
YU. D. Tretyakov, I. V. Gordev, and YA. A. Kesler, Journal Solid State Chem 20, 345-58, 1976.
Von G. Strick, G. Eulenberger and H. Hahn, Zeitschrift fur anorganische und allgemeine Chemie. Band 375,1968
J. Hubsch, G. Gavoille, and J. Bolfa, Journal. Appl. Phys. 49(3), 1978.
K.Belakroum, Magister thesis, Mentouri University,04
M. S. Park, S. K. Kwon, S. J. Youn, and B. I. Min, Phys Review B, Vol. 59, N° 15, 1998.
M. S. Park, S. K. Kwon, and B. I. Min, Phys Review B, Vol. 64, 100403(R), 2001.
J.-S. Kang, S. J. Kim, C. S. Kim, C.G. Olson, and B. I. Min. Phys Review B, Vol. 63, 144412, 2000.
S. J. Kim, W. C. Kim and C. S. Kim, Journal of Magnetic and Magnetic Materials 242-245, 2002.
E.L. Nagaev, Physics Reports 346, 387-531, 2001.
J. B. Goodenough, Solid State Commun. 5, 577, 76.
J.B.Goodenough, J.Phys. Chem.Solids 30, 216, 1969.
F. K. Lotgring, R. P. Van Stapele, G.H.A.M.Van det Steen, and J. S. Van Wieringen, J.Phys. Chem.Solids 30, 799, 1969.
J. C. Th. Holland, G. Sawatzky, and C. Haas, Solid State Commun. 15, 747, 1974.
Z. W. Lu, B. M. Klein, E. Z. Kurmaev, V. M. Cherkashenko, V. R. Galakhov, S. N. Shamin, Yu M. Yarmoshenko, V. A. Trofimova, St. Uhlenbrock, M. Neumann, T. Furubayashi, T. Furubayashi, T. Hagino,
And S. Nagata, Phys, Rev. B 53, 9626, 1996.
G. L. W. Hart, W. E. Pickett, E. Z. Kurmaev, D. Hartmann, M. Neumann, A. Moewes, D. L.Ederer, R. Endoh, K. Taniguchi, and S. Nagata, Phys. Rev. B 61,
M. M.Ballal and C. Mande, Solid State Commun. 19, 325, 1976.
P. R. Locher, Solid State Commun. 5, 185, 1967.
C. Colominas, Phys. Rev. 153, 558, 1967.
J. Krok-Kowalski, T. Gron, J. Warczewski, T. Mydlarz, and I. Okonska-Kozlowska, J. Magn. Magn. Mater. 168, 129, 1997.
R. W. Cahn, P. Haasen, E. J. Kramer, Materials Science and Technology Vol. 3A, Ed. VCH, 1994.
R.Chevrel, J. Guillevic, M. Sergent, C. R. Acad. Sci. C, 1970, 271, p.1240.