EFFECT OF THE SINTERING ON MICROSTRUCTURE AND SUPERCONDUCTING PROPERTIES OF YBA2CU3O7-δ CERAMICS
الكلمات المفتاحية:
YBa2Cu3O7-δ high-Tc superconductors، X-ray diffraction (XRD)، scanning electron microscopy (SEM)، thermal analysis (TDA-TGA)، Sinteringالملخص
Superconducting YBa2Cu3O7-δ (Y-123) ceramics were prepared by the solid-state reaction method. The microstructure and superconducting properties of the sintered samples obtained under various conditions were investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), thermal analysis (TDA-TGA) and electrical resistivity
measurements. The study showed that the calcination at 800°C for 30 hours of theY2O3, BaCO3 and CuO mixture led to the starting of the Y-123 and BaCuO2 phases’ formation. However, in the temperature range of 950 - 990°C, Y-123 crystallized and became predominate compound. For
higher temperatures (near 1100°C), green Y2BaCuO5 phase was formed. A (00l) preferred orientation of Y-123 grains was occured after sintering in air at temperatures 950-990°C for 30 hours. The textured samples presented the best transport properties
التنزيلات
المراجع
- J.G. Huber, W.J. Liverman, Y. Xu, and A.R. Moodenbaugh,
Phys. Rev. B 41, 8757 (1990).
- C.O. Kim, and J.C. Park, J. Mater. Res. 13, 2067 (1998).
- M.F. Imayev, D.B. Kazakova, A.N. Gavro, and A.P. Trukhan,
Physica C 329, 75 (2000).
- A. Nishida, N. Fuketa, K. Furuya, and K. Horia, Jpn. J. Appl.
Phys. 33, 4583 (1994).
- A.Koblischka et Al, Supercond. Sci. And Technol. 18, S158-
S163 (2005).
- A.J. Jacobson, J.M. Newsam, D.C. Johnson, D.P. Gorshorn, J.T.
Lewandowski, and M.S. Alvarez, Phys. Rev. B 39, 254 (1989).
- S. Glenis, G. Choi, C.L. Lin, T. Mihalisin, and X.Q. Wang, J.
Appl. Phys. 79, 5873 (1996).