EFFECT OF THE SINTERING ON MICROSTRUCTURE AND SUPERCONDUCTING PROPERTIES OF YBA2CU3O7-δ CERAMICS

Auteurs-es

  • M MAHTALI Université de Constantine 1
  • A BOUBEGHAL Université de Constantine 1
  • A BOUABELLOU Université de Constantine 1

Mots-clés :

YBa2Cu3O7-δ high-Tc superconductors, X-ray diffraction (XRD), scanning electron microscopy (SEM), thermal analysis (TDA-TGA), Sintering

Résumé

Superconducting YBa2Cu3O7-δ (Y-123) ceramics were prepared by the solid-state reaction method. The microstructure and superconducting properties of the sintered samples obtained under various conditions were investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), thermal analysis (TDA-TGA) and electrical resistivity
measurements. The study showed that the calcination at 800°C for 30 hours of theY2O3, BaCO3 and CuO mixture led to the starting of the Y-123 and BaCuO2 phases’ formation. However, in the temperature range of 950 - 990°C, Y-123 crystallized and became predominate compound. For
higher temperatures (near 1100°C), green Y2BaCuO5 phase was formed. A (00l) preferred orientation of Y-123 grains was occured after sintering in air at temperatures 950-990°C for 30 hours. The textured samples presented the best transport properties

Téléchargements

Les données relatives au téléchargement ne sont pas encore disponibles.

Bibliographies de l'auteur-e

M MAHTALI, Université de Constantine 1

Laboratoire des Couches Minces et Interfaces

A BOUBEGHAL, Université de Constantine 1

Laboratoire des Couches Minces et Interfaces

A BOUABELLOU, Université de Constantine 1

Laboratoire des Couches Minces et Interfaces

Références

- J.G. Huber, W.J. Liverman, Y. Xu, and A.R. Moodenbaugh,

Phys. Rev. B 41, 8757 (1990).

- C.O. Kim, and J.C. Park, J. Mater. Res. 13, 2067 (1998).

- M.F. Imayev, D.B. Kazakova, A.N. Gavro, and A.P. Trukhan,

Physica C 329, 75 (2000).

- A. Nishida, N. Fuketa, K. Furuya, and K. Horia, Jpn. J. Appl.

Phys. 33, 4583 (1994).

- A.Koblischka et Al, Supercond. Sci. And Technol. 18, S158-

S163 (2005).

- A.J. Jacobson, J.M. Newsam, D.C. Johnson, D.P. Gorshorn, J.T.

Lewandowski, and M.S. Alvarez, Phys. Rev. B 39, 254 (1989).

- S. Glenis, G. Choi, C.L. Lin, T. Mihalisin, and X.Q. Wang, J.

Appl. Phys. 79, 5873 (1996).

Téléchargements

Publié-e

2005-06-01

Comment citer

MAHTALI, M., BOUBEGHAL, A., & BOUABELLOU, A. (2005). EFFECT OF THE SINTERING ON MICROSTRUCTURE AND SUPERCONDUCTING PROPERTIES OF YBA2CU3O7-δ CERAMICS. Sciences & Technologie. A, Sciences Exactes, (23), 39–42. Consulté à l’adresse https://revue.umc.edu.dz/a/article/view/179

Numéro

Rubrique

Articles

Articles les plus lus du,de la,des même-s auteur-e-s

Articles similaires

1 2 3 4 5 6 7 > >> 

Vous pouvez également Lancer une recherche avancée d’articles similaires à cet article.