ANALYSIS OF THE HEATING EFFECT ON HIGH PERFORMANCE MORTAR THROUGH 2D IMAGES OF X-RAY MICRO-TOMOGRAPHY AND SEM MICROSCOPY
Résumé
The paper deals with the application of the X-ray micro-tomography technique to study high performance mortar notched test specimens first, after bending tests at room and hot conditions (700°C) and second, after just heating at 500°C. The scanning parameters were set to view all the test specimen transverse square section of 25 mmin side. In these conditions, a part of the material real porosity, supposed to be representative, was accessible. 2D and 3D reconstructed images were obtained and analysed. Hence, among the various microstructure parameters considered, the homogeneity of the porosity along the specimen was especially analysed through the pore area fraction parameter and discussed. A sensible increase in porosity of the areas surrounding the notch plane was observed and this result is probably related to the preparation of the specimen. The impact on the validity of bending tests performed on such notched specimens was also examined. Lastly the ability of this technique to evaluate temperature effect on porosity in these particular conditions was discussed in the light of complementary analysis of SEM micrographs.
Références
Francois Renard, Dominique Bernard, Jacques Desrues, Erwan Plougonven, Audrey Ougier-Simonin. Characterisation of hydraulic fractures in limestones using X-ray microtomography. 2006 GeoX Conference, page 1 to 6.
J.-Y. Buffiere, H. Proudhon, E. Ferrie, W. Ludwig, E. Maire, P. Cloetens. Three dimensional imaging of damage in structural materials using high resolution micro-tomography. Nuclear Instruments and Methods in Physics Research B 238 (2005) 75–82.
Yohann Ledru, Robert Piquet, Laurent Michel, Fabrice Schmidt, Gerard Bernhart. 2-D and 3-D void quantification with image analysis in aeronautic composite laminates. Comptes Rendus des JNC 16 – Toulouse 2009.
1. Ellodie Boller, Peter Cloetens, Jose Baruchel, Jeremie Pourchez. Synchroton X-Ray microtomography: a high resolution, fast and quantitative tool for rock characterization. Road Materials and Pavement Design, Volume X – No. X/2001, pages 1 to 9.
A. Stienon, A. Fazekas, J-Y. Buffière, A. Vincent, P. Daguier, F. Merchi. Materials Sciences and Engineering A, 513-514 (2009) 376-383.
Nicolas Burlion, Dominique Bernard, Da Chen. X-ray microtomography. Application to microstructure analysis of a cementitious material during leaching process. Cement and Concrete research 36 (2006) 146 - 157.
Téléchargements
Publié-e
Comment citer
Numéro
Rubrique
Licence
Les auteurs publiant dans cette revue acceptent les termes suivants :- Les auteurs détiennent le droit d'auteurs et accordent à la revue
le droit de première publication, avec l’ouvrage disponible simultanément [SPÉCIFIER LA PÉRIODE DE TEMPS] après publication, sous la licence Licence d’attribution Creative Commons qui permet à d'autres de partager l'ouvrage en en reconnaissant la paternité et la publication initiale dans cette revue. - Les auteurs peuvent conclure des ententes contractuelles additionnelles et séparées pour la diffusion non exclusive de la version imprimée de l'ouvrage par la revue (par ex., le dépôt institutionnel ou la publication dans un livre), accompagné d'une mention reconnaissant sa publication initiale dans cette revue.
- Les auteurs ont le droit et sont encouragés à publier leur ouvrage en ligne (par ex., dans un dépôt institutionnel ou sur le site Web d'une institution) avant et pendant le processus de soumission, car cela peut mener à des échanges fructueux ainsi qu'à un nombre plus important, plus rapidement, de références à l’ouvrage publié (Consulter The Effect of Open Access).