Keywords
powder metallurgy
NDT
Eddy current
Magnetic measurement
How to Cite
Abstract
NDT Magnetic measurements as impedance in Eddy currents, corecitif and residual field in hysteresis loop are used to study the different stages of mechanical alloying in the Fe–Co system. In this paper, we changed the electromagnetic properties of Fe-Co, by developing their metallurgical parameters such as grain size. For this we are used a planetary ball mill, we are milled the FeCo alloy for different milling times until to obtain nanostructure, the lamellar structure with some small particles embedded in them was observed during the first stage of mechanical alloying. XRD patterns show after 10 h of milling the formation of a disordered solid solution having a body-centered cubic (bcc) structure. After 40h of milling, morphological studies indicated that the average crystallites size is around 15 nm.References
. C. Suryanarayana, E. Ivanov and V.V.Boldyrev,Materials Sci. and Eng. A304–306, 151–158 (2001).
. J.S. Benjamin, Metallurgical Transaction 1 2943 (1970). 3.
. Karimi L., Shokrollahi H., (2011) j.Alloys Compd., 509, pp.6571-6577. Applied Sciences 6 (4),
. T. Sourmail, Prog. Mater. Sci. 50 (2005) 816–880.
. R.H. Yu, S. Basu, R.Y. Zhang, A. Parvizi-Marjidi, IEEE Trans Magn 36(5) (2000) 388–93.
. Lesile-Pelecky, D.L. Rieke, R.D. (1996), ‘’Magnetic properties of nanostructured materials’’, Chem. Mater. 8 (8) 1770–1783.
. Herzer. G. (1996) Nanocrystalline soft magnetic materials, J. Magn. Magn. Mater. 157/158 133–136.
. Gleiter H. (1995) Nanostructured materials: state of the art and perspective, Nanostruct. Mater. 6) 3–14.
. M.Zergoug, H.Oubouchou and N.Amimeur, American J. of Applied Sciences 6 (4), 752-756. (2009).
. Yu R.H., Basu S., Zhang Y. Xiao J.Q, (2000) Magnetic domains and coercivity in FeCo soft magnetic alloys, J. Appl. Phys. 85 (8) 6034–6036.
. Fecht H.J., (1995) Nanostructure formation by mechanical attrition, Nanostruct. Mater. 6 33–42.
. O’Handley RC. (2000) Modern magnetic materials (principles and applications). Wiley– Interscience, p. 367.
. Bahrami A, Madaah Hosseini HR. (2005) Preparation of nanocrystalline Fe–Si–Ni soft magnetic powders by mechanical alloying. Mater Sci Eng B;123:74.
. Turgut Z., Scott, J.H.M.Q. Huang, Majetich S.A., Mchenry M.E., (1998)Magnetic properties and ordering in C-coated FexCo1 x alloy nanocrystals, J. Appl. Phys. 83 (11) 6468–6470.
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Copyright (c) 2019 Sciences & Technology